Polycarbonate
" is made of bisphenol A, which is a polymer material of polycarbonate. It has excellent high transparency and heat resistance temperature, as well as the highest impact strength of thermal plasticity resin, and good formability
"
Polycarbonate
" is the best material of choice for replacing metal supplies for automobile components, business machines, home appliances,electronic parts, food appliances, medical equipment and communication equipment.
Contact us For product pricing, customization, or other inquiries:
Contact Us
Explore More Products
- Product Details
- {{item.text}}
Quick Details
-
Brand Name:
-
Covestro/Makrolon
-
Material:
-
Polycarbonate PC Resin
-
Type:
-
Engineering Resin
-
Package:
-
25Kg/Bag
Quick Details
-
color:
-
Opaque
-
Shape:
-
Granules
-
Place of Origin:
-
Guangdong, China
-
Brand Name:
-
Covestro/Makrolon
-
Material:
-
Polycarbonate PC Resin
-
Type:
-
Engineering Resin
-
Package:
-
25Kg/Bag
Covestro Makrolon Polycarbonate
Place of Origin：China
Brand Name：Covestro/Makrolon
Model Number：9417
Featured：Flame retardant, Dimensionally stable, UV stable
Quality：High-quality
Application：General
Keywords：Covestro 9417/ Makrolon 9417/ Covestro Makrolon 9417
Material：Polycarbonate, 100% Vrigin PC Material
Brand：Covestro makrolon
Brand Name：Covestro/Makrolon
Model Number：9417
Featured：Flame retardant, Dimensionally stable, UV stable
Quality：High-quality
Application：General
Keywords：Covestro 9417/ Makrolon 9417/ Covestro Makrolon 9417
Material：Polycarbonate, 100% Vrigin PC Material
Brand：Covestro makrolon
Product Description
Makrolon® 9417
MVR (300 °C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV stabilized; easy release
MVR (300 °C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV stabilized; easy release
Rheological properties
|
Property
|
|
Test Condition
|
Unit
|
Standard
|
typical Value
|
|
|
C
|
Melt volume-flow rate
|
300 °C/ 1.2 kg
|
cm³/10 min
|
ISO 1133
|
6.0
|
|
|
|
Melt mass-flow rate
|
300 °C/ 1.2 kg
|
g/10 min
|
ISO 1133
|
7.0
|
|
|
C
|
Molding shrinkage, parallel
|
60x60x2 mm/ 500 bar
|
%
|
ISO 294-4
|
0.6
|
|
|
C
|
Molding shrinkage, normal
|
60x60x2 mm/ 500 bar
|
%
|
ISO 294-4
|
0.45
|
|
|
|
Molding shrinkage, parallel/normal
|
Value range based on general
practical experience |
%
|
b.o. ISO 2577
|
0.4-0.6
|
|
Mechanical properties (23 °C/50 % r. h.)
|
Property
|
|
Test Condition
|
Unit
|
Standard
|
typical Value
|
|
|
C
|
Tensile modulus
|
1 mm/min
|
MPa
|
ISO 527-1,-2
|
3800
|
|
|
|
Yield stress
|
50 mm/min
|
%
|
ISO 527-1,-2
|
64
|
|
|
|
Yield strain
|
50 mm/min
|
MPa
|
ISO 527-1,-2
|
4.6
|
|
|
C
|
Stress at break
|
50 mm/min
|
MPa
|
ISO 527-1,-2
|
45
|
|
|
C
|
Stress at break
|
50 mm/min
|
%
|
ISO 527-1,-2
|
15
|
|
|
C
|
Tensile creep modulus
|
1 h
|
MPa
|
ISO 899-1
|
3600
|
|
|
C
|
Tensile creep modulus
|
1000 h
|
MPa
|
ISO 899-1
|
2900
|
|
|
|
Flexural modulus
|
2 mm/min
|
MPa
|
ISO 178
|
3600
|
|
|
|
Flexural strength
|
2 mm/min
|
MPa
|
ISO 178
|
105
|
|
|
|
Flexural strain at flexural strength
|
2 mm/min
|
%
|
ISO 178
|
5.8
|
|
|
|
Flexural stress at 3.5 % strain
|
2 mm/min
|
MPa
|
ISO 178
|
95
|
|
|
C
|
Charpy impact strength
|
23 °C
|
kJ/m²
|
ISO 179/1eU
|
150C(N)
|
|
|
|
Charpy impact strength
|
-60 °C/3mm
|
kJ/m²
|
ISO 179/1eU
|
100C
|
|
|
|
Charpy notched impact strength
|
-30 °C/3mm
|
kJ/m²
|
ISO 21305/based on ISO 179/A
|
10C
|
|
|
|
Izod notched impact strength
|
23 °C/3mm
|
kJ/m²
|
ISO 21305/based on ISO 180/A
|
8C
|
|
|
C
|
Puncture impact properties - maximum force
|
23 °C
|
N
|
ISO 6603-2
|
4000
|
|
|
C
|
Puncture impact properties - maximum force
|
-30 °C
|
N
|
ISO 6603-2
|
3700
|
|
|
C
|
Puncture energy
|
23 °C
|
J
|
ISO 6603-2
|
25
|
|
|
C
|
Puncture energy
|
-30 °C
|
J
|
ISO 6603-2
|
15
|
|
|
|
Ball indentation hardness
|
|
N/mm²
|
ISO 2039-1
|
128
|
|