Quick Details
-
CaO Content (%):
-
33%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
0
-
Place of Origin:
-
Henan, China
-
Model Number:
-
Sintering refractory bricks for steelmaking
-
Brand Name:
-
Lite
-
Product name:
-
Sintering and oil immersion dolomite refractory bricks for steelmaking
-
Apparent porosity:
-
3% Max
-
Size:
-
230*114*65mm
-
Cold crushing strength:
-
62 MPa Min
-
Feature 2:
-
Can not contact with acid refractory material
-
Reheating Linear Change(1650 °C,2h):
-
0~-0.4% Max
-
Feature 3:
-
Resist basic (alkaline) slag
-
Refractoriness under load, 0.2MPa:
-
1700°C Min
-
Feature 1:
-
Good anti-corrosiveness
Quick Details
-
SiO2 Content (%):
-
3.5% Max
-
Al2O3 Content (%):
-
0
-
MgO Content (%):
-
66%
-
CaO Content (%):
-
33%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
0
-
Place of Origin:
-
Henan, China
-
Model Number:
-
Sintering refractory bricks for steelmaking
-
Brand Name:
-
Lite
-
Product name:
-
Sintering and oil immersion dolomite refractory bricks for steelmaking
-
Apparent porosity:
-
3% Max
-
Size:
-
230*114*65mm
-
Cold crushing strength:
-
62 MPa Min
-
Feature 2:
-
Can not contact with acid refractory material
-
Reheating Linear Change(1650 °C,2h):
-
0~-0.4% Max
-
Feature 3:
-
Resist basic (alkaline) slag
-
Refractoriness under load, 0.2MPa:
-
1700°C Min
-
Feature 1:
-
Good anti-corrosiveness
Product Description
Product Features
1. High refractoriness, multiply mineral composition;
2. Good thermal conductivity, strong slag erosion resistance.
2. Good thermal conductivity, strong slag erosion resistance.
|
Material
|
|
Magnesia
|
|
|
|
|
|||||
|
Name of product
|
|
Dense magnesia
brick
|
|
Magnesia brick
|
Medium grade magnesia brick
|
Light weight magnesia brick
|
|||||
|
Brand
|
|
MZ-91
|
MZ-89
|
MZ-87
|
ZMZ-93
|
BQM-89
|
|||||
|
Chemical composition,%
|
MgO
|
91
|
89
|
87
|
93
|
89
|
|||||
|
|
CaO≤
|
3.0
|
3.0
|
3.0
|
1.5
|
3.5
|
|||||
|
Refractoriness,℃
|
|
-
|
-
|
-
|
-
|
≥2.15
|
|||||
|
AP%≤
|
|
18
|
20
|
20
|
16
|
40
|
|||||
|
Cold crushing strength,MPa
|
|
58.8
|
49.4
|
39.2
|
70
|
8.5
|
|||||
|
Permanent linear change%1500℃*2h
|
|
0-0.5
|
0-0.6
|
-
|
0-0.2
|
-
|
|||||
|
Refractoriness iness under 0.2MPa load
|
|
≥1550
|
≥1540
|
≥1520
|
≥1610
|
-
|
|||||
|
Characteristic
|
|
Resistance to basic slag corrosion
|
Resisrance to basic slag corrosion
|
Resistance to high temperature
|
Resistance to high temperature and basic slag corrosion
|
Heat insulation ang high temperature resistance
|
|||||
|
Main application
|
|
Permanent layer of converter and other klin&furnace
|
Permanent layer of converter and other klin&furnace
|
Permanent layer of converter and other klin&furnace
|
High temperature basic kiln&fernace
|
Permanent layer of top cone and body of converter
|
|||||