Contact us For product pricing, customization, or other inquiries:
Contact Us
Explore More Products
- Product Details
- {{item.text}}
Quick Details
-
CaO Content (%):
-
2%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
0
-
Place of Origin:
-
China
-
Model Number:
-
zq0908
-
Brand Name:
-
YUTONG
-
Fe2O3 %:
-
2.5 max
-
Refractoriness ℃:
-
1740 min
-
Refractoriness under load (0.2MPa) ℃:
-
1350 min
-
Apparent porosity %:
-
24 max
-
Cold crushing strength Mpa:
-
30 min
-
Application:
-
Insulation,refractory
-
Size:
-
230*114*65mm
-
Usage:
-
Furnace Liner
-
Product name:
-
Competitive price curved fire clay brick for refractory industry
-
Color:
-
Yellow
Quick Details
-
SiO2 Content (%):
-
50%~65%
-
Al2O3 Content (%):
-
38-42%
-
MgO Content (%):
-
0.8-1.2
-
CaO Content (%):
-
2%
-
CrO Content (%):
-
0
-
SiC Content (%):
-
0
-
Place of Origin:
-
China
-
Model Number:
-
zq0908
-
Brand Name:
-
YUTONG
-
Fe2O3 %:
-
2.5 max
-
Refractoriness ℃:
-
1740 min
-
Refractoriness under load (0.2MPa) ℃:
-
1350 min
-
Apparent porosity %:
-
24 max
-
Cold crushing strength Mpa:
-
30 min
-
Application:
-
Insulation,refractory
-
Size:
-
230*114*65mm
-
Usage:
-
Furnace Liner
-
Product name:
-
Competitive price curved fire clay brick for refractory industry
-
Color:
-
Yellow
Competitive price curved fire clay brick for refractory industry
| Index | |
| Al2O3 % | 42 - 45 |
| Fe2O3 % | |
| Refractoriness ℃ | |
| Refractoriness under load (0.2MPa) ℃ | |
| Linear change on reheating %(1400℃, 2h) | |
| Apparent porosity % | |
| Cold crushing strength Mpa | 30 min |
| Payment terms | |
| Delivery time | Shipped in 30 days after payment |